Abstract
The investigation of the graphene (GN) performance in improving mechanical properties of recycled polypropylene with crosslinkedpolyaniline (rPP-g-PANI) was prepared via ultrasound extrusion. The concentration of GN in the research was varied from 0.5 to 3 phr, while polyaniline (PANI) and dycumil peroxide(DCP) were fixed at 4 wt. % and 1 phr loading, respectively. The morphological structure of the nanocomposites was investigated using fill emission scanning electron microscopy (FESEM) and confirmed a good dispersion of PANI and GN on rPP matrix. The increasing loading of GN has promoted a slight improvement in tensile modulus and tensile strength at 1.5 and 2 phr of GN loadings, respectively. However elongation at break showed a decrease at all PANI loadings due to lack of interfacial addition between PANI/GN particles and the rPP matrix.