Abstract
Unbalanced magnetron sputtering deposition of C-H films has been performed with various levels of negative substrate bias and with a fixed flow rate of hydrogen. Argon was used as a sputtering gas and formed the majority of the gas in the plasma. The effect of hydrogenation on the final concentration of trapped elements and their thermal stability with respect to hydrogen content is studied using ion beam analysis (IBA) techniques. The elemental concentrations of the films were measured in the films deposited on silicon substrates with a 2.5 MeV of H+ beam, which is used to perform Rutherford Backscattering Spectrometry (RBS) and Non-Rutherford Backscattering spectrometry (NRBS) and with 16 MeV of O5+ beam, used to perform Elastic Recoil Detection Analysis (ERDA). Effect of bias on the thermal stability of trapped hydrogen in the films has been studied. As the films were heated in-situ in vacuum using a non-gassy button heater, hydrogen was found to be decreasing around 400 degrees C.