Abstract
In this study, composite of Themoplastic polyurethane (TPU) reinforced with short fiber (Hibiscus Cannabinus) kenaf (KF) were prepared via melt blending method using Haake Polydrive R600 internal mixer. Effect of various processing temperatures, times and speeds on tensile strength was studied, together with effect of various fiber sizes on tensile, flexural properties and impact strength. Optimum blending parameters were 190 degrees C, 11 min, and 40 rpm for temperature, time and speed, respectively. Using the optimum processing parameters TPU-KF composites with different fiber sizes were prepared. Composite sheets were prepared by hot press machine at 190 degrees C for 10 min. Five samples were cut from the composite sheet. Mean value was taken for each composite according to ASTM standards. Tensile and flexural strength were best for fibers between 125-300 micron. Impact strength showed an increasing trend with increasing fiber size.