Abstract
Nano-size Al(2)O(3) (40 nm) addition effect on the polycrystalline (Bi, Pb)-2223 system properties was studied by XRD, SEM, TEM/EDX and electrical measurements. Samples with 0.0 and 0.2. wt% Al(2)O(3) are synthesized in air by solid state reaction. Nanometer Al(2)O(3) particles were added during the final sintering cycle of a multi-step preparation process. Analysis of magnetoresistivity has shown that the dissipation phenomenon follows the thermally activated flux creep model. Both onset temperature of dissipation, effective activation energy U, critical current density J(c) behaviour in applied magnetic field and volume pinning force density F(p) are enhanced by addition of 0.2wt.% Al(2)O(3). Enhancement of the vortices flux pinning in doped samples is mainly originated from the surface normal-like pinning centers.