Abstract
Thin films of lanthanum phosphate (LaPO4) nanostructures were fabricated on quartz substrate using sol-gel spin coating method subsequent with drying and annealing process. Increase of annealing temperature will increase the intensity of diffraction peaks; reveal that the particle size and crystallinity increase with temperature. A monoclinic structure was shown to be present in LaPO4 thin films after first anneal at 200 degrees C. The LaPO4 nanostructures of average size 30 - 50 nm were observed with field emission scanning electron microscopy. While the crystallize size were measured with x-ray diffraction (XRD). The images of LaPO4 nanostructure films show uniformity of samples with homogenously close-packed morphology.