Abstract
Fe-8Mn-6Si-13Cr-6Ni-12Co shape memory alloys are characterized by a good corrosion resistance and a modest shape memory effect. Experimental tests of the corrosion resistance of Fe-8Mn-6Si-13Cr-6Ni-12Co have been studied and compared with the Fe-32Mn-6Si alloy using weight loss, free corrosion and polarization resistance tests. The shape memory effect measurement of the Fe-8Mn-6Si-13Cr-6Ni-12Co and Fe-32Mn-6Si alloys has been also tested after 5% of deformation. The results of corrosion experimental tests show that the Fe-8Mn-6Si-13Cr-6Ni-12Co SMA is not very active in the Na2SO4 solution at pH4 at room temperature. In addition, its corrosion resistance is better than the Fe-32Mn-6Si and almost similar to the 316L stainless steel. To improve the shape memory effect of the Fe-8Mn-6Si-13Cr-6Ni-12Co, a thermomechanical treatment has been applied by 8% prestrain in tensile and followed by heat treatment at 1320K for 1 hour. The results show an improvement in the shape memory effect after 5% of deformation in tensile test.