Abstract
Photocurrent measurements for stainless steel type 304 in the as- received condition after DC and AV passivation have confirmed that significant changes of the passive film properties occur due to AV passivation. The photocurrents were the highest for the sample treated by the AV passivation process (AVPP). The bandgap energy increased from about 2.8 to about 3.05 eV for this treatment. Very similar results have been obtained for pure chromium, which suggests that the AVPP produces a thicker passive film with a less defective nature due to a partial dehydration of the chromium oxide phase in the film.