Abstract
We report a study of the optical signal amplification properties of Rhodamine 640 in solution, in thin-film format dispersed within a poly(methyl methacrylate) (PMMA) polymer matrix, and in a waveguiding structure created by coating polymer-dispersed Rhodamine 640 onto a patterned quartz substrate. The optical signal amplification experiments were carried out using a collinear pump and signal setup. Depending on both pump and signal energies, gains of up to 41 dB were achieved in solution, while 1% by weight dye-doped PMMA films showed net gains of
54
cm
−
1
, and associated losses of
16
cm
−
1
. Using the same concentration dye/PMMA dispersions, waveguide structures were fabricated with a
120
×
1
μ
m
2
cross section and a length of 1.2 cm. The internal optical gain values measured at 625 and 650 nm were found to be as high as 26 and 8 dB, respectively. The corresponding signal-to-noise ratio was in the 7-21-dB range at 625 nm and in the 3-21-dB range at 650 nm. Both in solution and in the waveguide structures we found that amplified spontaneous emission had a detrimental effect on the optical gain characteristics through a decrease in the signal-to-noise ratio.