Abstract
In this work, CeO2 nanoparticles, as well as CeO2 nanocomposites with plasmonic silver nanoparticles, were synthesized using a simple sol-gel process. The concentration of silver in the composites varied from 0.031-0.25 wt%. Cerium hydroxide dried gel was calcined at temperatures from 125 to 800 degrees C to obtain CeO2. It was shown that, at an annealing temperature of 650 degrees C, single-phase CeO2 nanopowders with an average particle size in the range of 10-20 nm can be obtained. The study of acid-base properties showed that with an increase in the calcination temperature from 500 to 650 degrees C, the concentration of active centers with pKa 9.4 and 6.4 sharply increases. An analysis of the acid-base properties of CeO2-Ag nanocomposites showed that with an increase in the silver concentration, the concentration of centers with pKa 4.1 decreases, and the number of active centers with pKa 7.4 increases. In a model experiment on dye photodegradation, it was shown that the resulting CeO2 and CeO2-Ag nanopowders have photocatalytic activity. CeO2-Ag nanocomposites, regardless of the silver concentration, demonstrated better photocatalytic activity than pure nanosized CeO2.