Abstract
The mitigation of the physical aging of thin-film composite (TFC) poly[1-trimethylsilyl-1-propyne] (PTMSP) membranes was studied via the simultaneous application of a polymer-selective layer crosslinking and mixed-matrix membrane approach. For the first time, a recently developed highly porous activated carbon material (infrared (IR) pyrolyzed poly[acrylonitrile] (PAN) or IR-PAN-a) was investigated as an additive to a PTMSP-selective layer for the reduction of aging in TFC membranes. The total electric energy spent on the IR irradiation treatment of IR-PAN-a particles was twice lower than conventional heating. The flat-sheet porous microfiltration membrane MFFK-1 was used as a support, and the crosslinked PTMSP/PEI loaded with a porous filler was applied as a selective layer (0.8-1.8 mu m thick) to the TFC membranes. The initial IR-PAN-a sample was additionally milled to obtain a milled IR-PAN-aM sample with a monomodal particle size distribution of 500-800 nm. It was shown that IR-PAN-a, as a filler material with a high surface area and pore volume (2450 m(2)/g and 1.06 cm(3)/g, respectively) and a well-developed sponge-like structure, leads to the increase of the N-2, O-2, and CO2 permeance of PTMSP-based hybrid membrane material and the decrease of the aging of PTMSP. The simultaneous effect of crosslinking and the addition of a highly porous filler essentially improved the aging behavior of PTMSP-based TFC membranes. The monomodal and narrow particle size distribution of highly porous activated IR-pyrolyzed PAN is a key factor for the production of TFC membranes with reduced aging. The highest stability was achieved by the addition of a milled IR-PAN-aM sample (10 wt%). TFC membrane permeance was 6300 GPU (30% of initial permeance) after 11,000 h of aging at ambient laboratory conditions.