Abstract
Effects of annealing and test temperatures on the tensile behavior of UNS N04400 alloy have been examined. The specimens were annealed at 800, 1000, and 1200 °C for 4 h under vacuum in a muffle furnace. Stress-strain curves of the specimens were obtained in the temperature range 25-300 °C using a universal testing machine fitted with a thermostatic chamber. The results indicate that the yield strength (YS), ultimate tensile strength (UTS), and percentage elongation of the specimens decrease with increase of annealing temperature. By increasing the test temperature, the YS and UTS decrease, whereas the percentage elongation initially decreases with increase of test temperature from 25 to 100 °C and then increases with further increasing the temperature up to 300 °C. The changes in the tensile properties of the alloy are associated with the post-annealing microstructure and modes of fracture.