Abstract
In this study, amorphous chalcogenide Cu
10Se
90 and Cu
20Se
80 thin films have been obtained by thermal evaporation deposition process on well-cleaned quartz substrates. Thin films were annealed at various temperatures in N
2 atmosphere. X-ray diffraction patterns (XRD) showed that the films are like amorphous in nature for as prepared but annealed films produced crystalline peaks and that their crystallinity was proportional to annealing temperature. Thin film morphologies were examined using scanning electron microscopy (SEM). The optical absorption coefficient (
α) for the as-deposited and annealed films was calculated using spectrophotometer measurements of the transmittance (
T) and reflectance (
R) at normal incidence of light in the wavelength range 200–2500
nm. The optical band gap (
E
g) was found to be around 2.281 and 2.231
eV for as-prepared Cu
10Se
90 and Cu
20Se
80 thin films respectively, (
E
g) showed a decrease with increasing of the annealing temperature higher than the glass transition temperature (
T
g). The high frequency dielectric constant (
ε
∞
) and the ratios of the carrier concentration to the effective mass (
N
/
m
*
) were also determined for the as-deposited and annealed films. The dispersion of the refractive index is discussed in terms of the single-oscillator model. The oscillator energy
E
o
and the dispersion energy
E
d were obtained. The results are discussed and correlated in terms of amorphous–crystalline transformations.