Abstract
The magnetocaloric effect along with magnetic phase transition in the peroveskite polycrystalline samples La0.7Ba0.2Ca0.1Mn1-xSnxO3 (x = 0 and 0.1) was investigated. The samples were synthesized using conventional solid state reaction at 1400 degrees C temperature. Magnetization vs. temperature measurements, under a magnetic field of mu H-0 = 0.05 T, showed a paramagnetic-ferromagnetic transition at Curie temperature, T-C, which decreases from 310 K for x = 0 -290 K for x = 0.1. A large magnetic entropy change vertical bar Delta S-M vertical bar deduced from isothermal magnetization curves, has been observed in our samples with a peak centered on their respective T-C. Interesting values of the relative cooling power (RCP), 237 J kg(-1) for x = 0 and 248 J kg(-1) x = 0.1, make these samples promising candidates for magnetic refrigeration around room temperature.