Abstract
The beneficial effects of V addition on the corrosion of a newly manufactured Ti6AlxV (x = 2 wt %, 4 wt %, 6 wt %, and 8 wt %) alloys after various exposure periods in 3.5% NaC1 solutions were reported. The Ti6AlxV were produced from their raw powders using mechanical alloying. Several electrochemical techniques such as electrochemical impedance spectroscopy, cyclic potentiodynamic polarization, and potentiodynamic current versus time at 300 mV experiments were conducted. The surface morphology and the elemental analysis were performed using scanning electron microscopy and energy dispersive X-ray analyses. All results were consistent with each other revealing that the increase of V content increases the resistance of the alloys against corrosion. The increase of corrosion resistance was achieved by the role of V in decreasing the rate of corrosion as a result of the formation of oxide films on the surface of the alloys. This effect was found to increase with prolonging the immersion time of the Ti6AlxV alloys in the test medium from 1 h to 24 h and further to 48 h.