Abstract
Many investigators have focused on the development of biocompatible polyurethanes by chemical reaction of functional groups contained in a spacer and introduced in the PU backbone or by a grafting method on graft polymerization of functional groups. In this study, alginate-based polyurethane (PU) composites were synthesized via step-growth polymerization by the reaction of hydroxyl-terminated polybutadiene (HTPB) and hexamethylene diisocyanate (HMDI). The polymer chains were further extended with blends of 1,4-butanediol (1,4-BDO) and alginate (ALG) with different mole ratios. The structures of the prepared PU samples were elucidated with FTIR and
H NMR spectroscopy. The crystallinity of the prepared samples was evaluated with the help of X-ray diffraction (XRD). The XRD results reveal that the crystallinity of the PU samples increases when the concentration of alginate increases. Thermogravimetric (TGA) results show that samples containing a higher amount of alginate possess higher thermal stability. ALG-based PU composite samples show more biocompatibility and less hemolytic activity. Mechanical properties, contact angle, and water absorption (%) were also greatly affected.