Abstract
Fourier-transform infrared (FTIR) spectroscopy is a fast and simple technique for functional group identification. This work provides a review and insight into the application and interpretation of FTIR spectroscopy for cementitious binders that comprise ordinary Portland cement, alkaline-activated binders, geopolymers, and material characterization for civil engineering material applications. This technique can be used to identify different compounds and a moiety of bond vibrations in inorganic molecules such as Si-O, -OH, H-O-H (water), C-O (carbonate or carbonation), aluminosilicate (Si-O-T, where T is Al or Si), and S-O (sulfate or gypsum) found in hydrated cement, alkaline binders, and geopolymers. The prominent bands include those representing carbonation (CO32- 1390-1475 cm(-1)), calcium carbonate (871, 1792-2516 cm(-1)), hydroxylation and water molecules (1607, 3400-3650 cm(-1)), strength skeletal framework compositions or Al-Si substitutions, silicate organization (C-A-S-H, N-A-S-H, or C-S-H (950-1055 cm(-1)), and sulfate (600-680, 1080-1100 cm(-1)). Some of the factors that could affect the spectra bands include elemental displacement due to changes in molar mass, activated temperature, pH, activator concentration, w/b ratio, Ca/Si ratio, Si/Al ratio, and the silica modulus (SiO2/Na2O) of the activators used in the binder synthesis. The method could be used for destructive and non-destructive testing on paste sample by using transmission and attenuated total reflectance methods, respectively.