Abstract
•Enamel conditioned with total-etch and rinse and bonded to metallic bracket (TER+MB) displayed the highest bond values.•The lowest value of shear bond strength (SBS) was exhibited by group 1 enamel conditioned with photodynamic therapy bonded to metallic bracket.•The most common failure type among investigated groups was adhesive.
To assess bond integrity and failure mode after enamel pretreated with conventional and contemporary conditioning methods were bonded to metallic brackets (MB).
Forty maxillary central incisors were selected and disinfected. All specimens were mounted up to the cement-o-enamel junction and divided into four experimental groups randomly based on the enamel conditioning technique. Photodynamic therapy (PDT) was used to condition enamel in group 1, Total-etch and rinse (TER) was used to treat samples in group 2, Specimens in group 3 were conditioned with ECL, and samples in group 4 surface pretreated with SEP. Bonding of MB was performed on the surfaces of all the specimens with a Transbond XT. Specimens from all investigated groups were positioned on a universal testing machine maintaining buccal surfaces similar to the direction of the force. After bracket debonding bond failure was assessed using ARI. The bond integrity of all four groups was compared using analysis of variance (ANOVA). Post hoc Tukey test was used for pairwise comparison among different groups.
Group 2, TER+MB (15.38±0.14 MPa) displayed the highest bond value whereas the lowest values of SBS were exhibited by group 1, PDT+MB (10.11±0.17 MPa). The inter-group comparison revealed that specimens of group 2 and group 3, ECL+MB (14.61±0.55 MPa) demonstrated comparable bond strength (p>0.05).
Enamel conditioned with TER and ECL demonstrated comparable SBS. However, bond integrity after PDT and SEP (self-etch primer) surface treatment of enamel bonded with MB significantly lowered bond values.