Abstract
Glasses of the composition 2TeO(2)-V2O5 were fabricated via the conventional melt-quenching technique. The amorphous and the glassy nature of the as-quenched samples were confirmed by X-ray powder diffraction (XRD) and differential scanning calorimetry (DSC), respectively. The glass transition and crystallization parameters were evaluated under non-isothermal conditions using DSC. X-ray diffraction studies confirmed the presence of partially oriented crystallites in the heat-treated glasses. Kauzmann temperature (lower bound for the kinetically observed glass transition) was deduced from the heating rate dependent glass transition and crystallization temperatures.