Abstract
[Display omitted]
•Efficient use of polymer waste as catalyst substrate.•Biopolymer coated sponge as host for synthesis of catalytic metal nanoparticles.•Reduction of environmental pollutants with high conversion rates.•Easy recovery of the catalyst and re-use.
In the present study, two catalysts based-on copper and nickel nanoparticles anchored on agarose-coated sponge (Cu-AG-sponge and Ni-AG-sponge) were prepared, respectively. Both catalysts were characterized by analytical techniques of thermogravimetric analysis energy dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM). Spherical Cu and Ni nanoparticles on struts of AG-coated sponge were observed by FESEM and the samples’ elemental composition was confirmed by EDX technique. After characterization, the Cu-AG-sponge and Ni-AG-sponge catalysts were tested in 4-nitrophenol (4-NP) and methylene blue dye (MB) reduction in an aqueous medium. The reduction of the 4-NP to 4-aminophenol (4-AP) was achieved up to 95% using the NaBH4 reductant and Cu-AG-sponge and Ni-AG-sponge catalysts, respectively. Similarly, the rate of reduction of MB was faster for the Cu-AG-sponge as compared to the Ni-AG-sponge which was discussed based-on the catalyst morphology and other factors. The high rate of reactions for the 4-NP and MB reduction suggests that the Cu-AG-sponge and Ni-AG-sponge catalyst possess high catalytic efficiency, low cost and good reusability having the potential to be used in similar other reactions.