Abstract
The effects of activating agent concentration on the pore structure and surface chemistry of activated carbons derived from olive stone with chemical activation method using phosphoric acid as the activating agent were studied. Mass changes associated with the impregnation, carbonization and washing processes were measured. With H3PO4 dilute solutions (60, 70, and 80 wt% H3PO4), the loading of substance on CS increases with concentration. The concentration of the H3PO4 solution seems to control the processes of impregnation, carbonization and washing in the preparation of AC from olive stones by H3PO4 chemical activation. ACs have been characterized from the results obtained by N-2 adsorption at 77 K. Moreover, the fractal dimension (D) has been calculated in order to determine the AC surface roughness degree. Optimal textural properties of ACs have been obtained by chemical activation with H3PO4 80 wt.%. The BET surface areas and total pore volumes of the carbons produced at H3PO4 80 wt.% are 1218 m(2)/g and 0.6 cm(3)/g, respectively. (C) 2011 Production and hosting by Elsevier B.V. on behalf of King Saud University.