Abstract
In this study, we synthesized and characterized a 3D network of silver nanowires (AgNWs), employing the polyol approach in ethylene glycol (EG) as the reductant and polyvinylpyrrolidone (PVP) as the structure-directing agent for the growth of AgNWs to design inexpensive, timely responsive AgNWs-based heaters with different substrates. Data obtained from a field emission scanning electron microscope (FESEM) revealed that the average diameter of the synthesized AgNWs was 22 nm, and the average length was 28 mu m. UV-visible absorption spectroscopy showed that AgNWs developed in a very pure phase. We investigated the impact of substrate type on the heating dissipation performance by depositing AgNW thin film over three chosen substrates made from readily available materials. The findings indicated that the AgNW-based heater with the wood substrate had the lowest response time of 21 s, the highest thermal resistance of 352.59 degrees C center dot cm(2)/W, and a steady temperature of 135 degrees C at a low bias voltage of 5 V compared to cement (95 s, 297.77 degrees C center dot cm(2)/W, and 120 degrees C) and glass (120 s, 270.25 degrees C center dot cm(2)/W, and 110 degrees C).