Abstract
This in vitro research aimed to evaluate the Tensile Bond Strength of Poly Ether Ether Ketone and Zirconia copings using resin cement with or without Visio.link adhesive. From commercially available Zirconia and PEEK, blocks were machined milled using (CAD)/(CAM) to obtain 20 Zirconia and 20 PEEK copings. These specimens were sandblasted using 110 mu m of alumina. The two main groups (20 Zirconia and 20 PEEK copings) were divided further into 4 subgroups, GROUP 1 (n = 10) PEEK substructure with self-adhesive resin cement without pretreatment, and GROUP 2 (n = 10) PEEK substructure with self-adhesive resin cement pre-treated with Visio.link adhesive. GROUP 3 (n = 10) Zirconia copings with self-adhesive resin cement without pretreatment. GROUP 4 (n = 10) Zirconia copings with self-adhesive resin cement pre-treated with Visio.link adhesive. Universal testing machine was used to evaluate the tensile bond strength of these copings. The results were analyzed using SPSS software Version 25.0 (SPSS Inc., Chicago, IL, USA). One-way ANOVA and independent t-test were used to compare the mean scores. Statistically significant increase was observed in Tensile Bond Strength of samples when Visio.link adhesive was used. Tensile Bond Strength of PEEK copings and Zirconia copings with Visio.link adhesive is considerably greater than PEEK copings and Zirconia copings without adhesive. The mean Tensile Bond Strength of Zirconia (with or without adhesive) is less as compared to Tensile Bond Strength of PEEK (with or without adhesive), but the difference is not statistically significant.