Abstract
Intense red upconversion luminescence was observed in the Er
/Yb
/Li
co-doped ZnGa
O
phosphor synthesized through the solid state reaction method for the first time. The structural characterization showed a large crystalline nature and an increase in the particle size
Li
doping. The absorption spectra showed a large number of peaks in the UV-vis-NIR regions due to the Er
and Yb
ions. The Er
/Yb
co-doped ZnGa
O
phosphor exhibited green, red and NIR upconversion emissions on excitation with 980 nm radiation. The intensity of the red emission was relatively larger than that of the other emissions. The luminescence intensity
pump power measurements revealed the number of required photons for these emissions. The phosphor showed very interesting color tunability as a function of Er
ion concentration and incident pump power. The luminescence intensity of the Er
/Yb
co-doped phosphor was enhanced more than two times
Li
doping. The enhancement in the luminescence intensity was proposed to be due to the increase in the crystallinity and particle size of the phosphor. The lifetimes of the
S
and
F
levels also increased in the presence of Li
ions. The variation in the fluorescence intensity ratio (FIR) of the thermally coupled levels (TCLs) of the red emission with incident pump power offered effective optical heating in the phosphor. The temperature-induced FIR using TCLs of red emission exhibited a larger value of temperature sensing sensitivity in the presence of Li
ions, which was up to 14 × 10
K
. Thus, the Er
/Yb
/Li
co-doped ZnGa
O
phosphor may be used in photonic, optical heating, and temperature sensing devices.