Abstract
Low-dimensional antimony-doped tin oxide aggregated nanoparticles (ATO NPs; dia. similar to 3.95 nm) were synthesized using hydrothermal method in alkaline phase. The optical, morphological, and structural properties of ATO NPs were characterized in details using FT-IR, UV/vis., FESEM, XEDS, XPS, TEM and XRD techniques. Glassy carbon electrode (GCE) was fabricated with a thin-layer of aggregated ATO NPs by, conducting coating binders (5% ethanolic nafion) for the development of selective and sensitive enzyme-less creatine sensors. Electrochemical responses along with higher sensitivity, large-dynamic range and long-term stability towards creatine were performed by electrochemical I-V approach. The calibration curve was found linear over a wide linear dynamic range (LDR) of creatine concentration (0.1 nM similar to 1.0 mM). From the gradient of the calibration plot, limit of detection (LOD) and sensitivity were calculated as 42.0 +/- 1 0.1 pM and 276.3 mu AmM-1 cm(-2) respectively. It is an organized route for the development of non enzymatic creatine sensor based on ATO NPs embedded GCE using electrochemical reduction phenomena and significantly applied for the real sample analyses. As far as we know, this report is the maiden publication on highly sensitive creatine sensor based on the ATO NPsiNafion/GCE. This method could be a pioneer development in creatine sensitive sensor development using ATO NPs in reliable I-V method for the important sensor applications with useful doped nanomaterials coupled nano-technological system. (C) 2016 Elsevier B.V. All rights reserved.