Abstract
Latex phase blending and crosslinking method was used in this research work to produce nitrile butadiene rubber-graphene oxide (NBR-GO) membranes. This fabrication technique is new and yields environmentally friendly membranes for oil-water separation. GO loading was varied from 0.5 to 2.0 part per hundred-part rubber (pphr) to study its effect on the performance of NBR-GO membrane. GO was found to alter the surface morphology of the NBR matrix by introducing creases and fold on its surface, which then increases the permeation flux and rejection rate efficiency of the membrane. X-Ray diffraction analysis proves that GO was well dispersed in the membrane due to the non-existence of GO fingerprint diffraction peak at 2 theta value of 10-12 degrees in the membrane samples. The membrane filled with 2.0 pphr GO has the capability to permeate 7688.54 Lm(-2) h(-1) water at operating pressure of 0.3 bar with the corresponding rejection rate of oil recorded at 94.89%. As the GO loading increases from 0.5 to 2.0 pphr, fouling on the membrane surface also increases from Rt value of 45.03% to 87.96%. However, 100% recovery on membrane performance could be achieved by chemical backwashing.