Abstract
Herein we report a well-organized analysis on various key-properties of SnS thin films for solar cell fabricated by nebulizer spray pyrolysis technique. X-ray diffraction study reveals the polycrystalline nature of deposited films with orthorhombic crystal structure. The crystallite size was calculated and observed to be in the range of 8–28 nm with increasing molarity of precursor solution. The stoichiometry composition of SnS was confirmed by EDX study. SEM/AFM studies divulge the well-covered deposited surface with spherical grains and the size of grains is increasing with concentration and so the roughness. A remarkable decrease in band gap from 2.6 eV to 1.6 eV was noticed by raising the molar concentration from 0.025 M up to 0.075 M. A single strong emission peak at about 825 nm is observed in PL spectra with enhanced intensity which may be attributed to near band edge emission. From the Hall effect measurement, it was found that the SnS thin film exhibits p-type conductivity. The calculated values of resistivity and carrier concentration are 0.729 Ω cm and 3.67 × 1018/cm3 respectively. Furthermore, to study the photovoltaic properties of SnS thin films a heterojunction solar cell, FTO/n-CdS/p-SnS was produced and the conversion efficiency was recorded about 0.01%.
[Display omitted]
•Nebulizer Spray Pyrolysis (NSP) technique is used to fabricate p-type SnS thin films.•Optical transparency of fabricated films was observed in the range of 60–80%.•Energy band gap is remarkable reduced from 2.6 eV to 1.6 eV by molar concentrations.•Values of ρ and n are found to be 7.29 × 10−1 Ω cm and 3.67 × 1018/cm3 respectively.•Good efficiency of fabricated solar cell was achieved.