Abstract
[Display omitted]
•Biopolymers based injectable hydrogels were fabricated by solution casting method.•Fabricated hydrogels were analyzed by FTIR, TGA, SEM and antimicrobial properties.•Swelling studies in different solvent media were also analyzed.•Release study of NMS loaded hydrogel in SIF and SGF solutions were examined.•NMS was released (83%) in a controlled manner confirming it as injectable hydrogel.
Silane crosslinked biopolymer based novel pH-responsive hydrogels were fabricated by blending the cationic (chitosan) and anionic (alginate) polymers with poly(vinyl alcohol). Tetraethoxysilane (TEOS) was used, as a crosslinker in different amounts due to its nonhazardous nature, to study its impact on physical and chemical properties of the prepared injectable hydrogels along with the controlled release of drug. The swelling response of the prepared hydrogels was examined in different solvent media which exhibited decreased swelling ratio with increase in the amount of TEOS. All the fabricated hydrogels represented highest swelling at acidic pH while low swelling at basic and neutral pH. This specific pH sensitive behavior at pH 7 made them an appropriate candidate for the injectable controlled drug delivery in which Neomycin Sulfate (NMS) was successfully loaded on suitable hydrogel (comprising 50μL TEOS) to study its release mechanism. The results revealed that in simulated gastric fluid (SGF), hydrogel released the entire drug (NMS) in initial 30min while in simulated intestinal fluid (SIF), NMS was released in a controlled way up to 83% in 80min. These results endorsed that the hydrogels could be practiced as a smart intelligent material for injectable controlled drug delivery as well as for other biomedical applications at physiological pH.