Abstract
Multi-walled carbon nanotubes (CNTs) were grown via pyrolytic chemical vapor deposition technique and explored for their infrared sensing behavior. CNT synthesis was carried out over cobalt zinc ferrite (Co0.5Zn0.5Fe2O4) catalyst nanoparticles under different gas flow conditions to control outside diameter of the nanotubes. It was found that a progressive decrease in the carbon precursor gas (acetylene in this case) from 5: 1 to 9: 1 (v/v) causes reduction of average CNT diameter from 85 nm to 635 nm. Growth conditions involving higher temperatures yield nanotubes/nanofibers with outer diameter of >500 nm, presumably due to surface aggregation of nanoparticles or increased flux of carbonaceous species at the catalyst surface or both. Current-voltage characteristics of the nanotubes depending on the CNT diameter, revealed linear or nonlinear behavior. When incorporated as sensing layer, the sensitivity of similar to 5.3 was noticed with response time of similar to 4.1 s. It is believed that IR sensing characteristics of such CNT-based detectors can be further enhanced through post-synthesis purification and chemical functionalization treatments.