Abstract
Aluminum oxide (Al2O3) are continuously demonstrating the functional characteristics in devices. The physiochemical properties of hydrothermally as-grown Aluminum oxide (Al2O3) have been investigated in this research article. The as-prepared material was confirmed as gamma- phase formation of Al2O3. The average crystallite size was found similar to 78 nm, whereas the particles were found in nano scale too. Moreover, the absence of impurity in EDS analysis, and the presence of the bending vibrations of Al-O-Al and Al-O band in FTIR characterization further confirmed the absence of impurity in the material. Evaluated dielectric properties such as a relatively high dielectric constant, and low dielectric loss indicated the good optical quality of gamma- Al2O3. Impedance and modulus spectroscopic studies showed the non-Debye type relaxation in gamma- Al2O3 with an average relaxation time of 5.8 mu s. Overall, the dielectric spectroscopy analysis of gamma- Al2O3 indicates the promising applications of gamma- Al(2)O(3 )in devices as dielectrics.