Abstract
Even with the demand for high esthetics, the strength of the material for esthetic applications continues to be important. In this study, monolith zirconia (MZi) crowns fabricated using CAD/CAM were tested for fracture resistance (FR) in teeth with class II cavity designs with varying proximal depths, restored through a deep marginal elevation technique (DME).
: Forty premolars were randomly divided into four groups of ten teeth. In Group A, tooth preparation was conducted and MZi crowns were fabricated. In Group B, mesio-occluso-distal (MOD) cavities were prepared and restored with microhybrid composites before tooth preparation and the fabrication of MZi crowns. In Groups C and D, MOD cavities were prepared, differentiated by the depth of the gingival seat, 2 mm and 4 mm below the cemento-enamel junction (CEJ). Microhybrid composite resin was used for DME on the CEJ and for the restoration of the MOD cavities; beforehand, tooth preparations were conducted and MZi crowns were and cemented using resin cement. The maximum load to fracture (in newtons (N)) and FR (in megapascals (MPa)) were measured using the universal testing machine.
The average scores indicate a gradual decrease in the load required to fracture the samples from Groups A to D, with mean values of 3415.61 N, 2494.11 N, 2108.25 N and 1891.95 N, respectively. ANOVA revealed highly significant differences between the groups. Multiple group comparisons using the Tukey HSD post hoc test revealed that Group D had greater DME depths and showed significant differences compared with Group B.
FR in teeth decreased when more tooth structure was involved, even with MZi crowns. However, DME up to 2 mm below the CEJ did not negatively influence the FR. Strengthening the DME-treated teeth with MZi crowns could be a reasonable clinical option, as the force required to fracture the samples far exceeded the maximum recorded biting force for posterior teeth.