Abstract
Silicon and iron aluminide (FeAl) nanoparticles were synthesized by a laser vaporization controlled condensation (LVCC) method. The particles generated by the laser ablation of solid targets were transported and deposited in the presence of well-defined thermal and electric field in a newly designed flow-type LVCC chamber. The deposition process of nanoparticles was controlled by the balance of the external forces; i.e., gas flow, thermophoretic and electrostatic forces. The size distributions of generated nanoparticles were analyzed using a low-pressure differential mobility analyzer (LP-DMA). The effect of synthesis condition on the size distribution was analyzed by changing the pressure of the carrier gas (20-200 Torr), the temperature gradient in the LVCC chamber (Delta T=0-190 degrees C) and the electric field applied between the LVCC chamber plates (E=0-3000 V/m). It was found that electrostatic field was effective to selectively deposit small size nanoparticles (about 10 nm) with expelling large droplet-like particles.