Abstract
In this work, undoped and Cr-doped single-crystalline ZnO nanorods were prepared by a facile microwave assisted solution method. X-ray diffraction (XRD) and transmission electron microscopy (TEM) results showed that Cr-doped ZnO was comprised of single phase nature with hexagonal wurtzite
structure up to 5% Cr doping, however, secondary phase ZnCr2O4 appeared upon further increasing the Cr dopant concentration. Field emission scanning electron microscopy (FESEM) and TEM micrographs suggested that the undoped nanorods with an average length of ∼2 μm
and a diameter in the range of 150-200 nm, respectively were observed. Interestingly, the size of nanorods decreased with the increase of Cr concentration in ZnO. Optical studies depicted that the energy bandgap was decreased with the increase of Cr concentration. Raman scattering spectra
of Cr-doped ZnO revealed the lower frequency shift of Ehigh2 phonon mode with the increase in concentration of Cr dopant, suggested the successful doping of Cr into Zn site in ZnO. Magnetic studies showed that Cr-doped ZnO exhibited room temperature ferromagnetism
(RTFM) and the value of magnetization was continuously decreased with the increase in Cr doping.