Abstract
Hydroxyapatite (HAP) containing different contents of palladium (Pd) ions were synthesized using the co-precipitation method. The structural and morphological properties of the assynthesized compositions were investigated using XRD and FESEM. The c/a increased from 0.728 to 0.733 with the lowest and highest contributions of Pd(II), respectively. Furthermore, the morphological features were investigated using FESEM. It was illustrated that Pd-HAP was formed as agglomerated as rod shapes with dimensions in the range of 63.4-110.3 nm for no Pd additions, and the size was reduced reaching 43.4-70.5 nm for the highest Pd contribution. Besides, the maximum height of the roughness (R-t) grew from 183.6 up to 236.5 nm for the lowest and highest Pd (II). Besides, the obtained specific surface area was around 28.3, 42.0, and 63.4 m(2)/g for 0.0Pd-HAP, 0.6Pd-HAP, and 1.0Pd-HAP, respectively. The antibacterial activity was examined against both Escherichia coli (E-coli) and Staphylococcus aureus (S. aureus), and it obvious that the activity was enhanced upon Pd content. The inhibition zone was increased from no sensitivity reaching 4.3 +/- 0.9 and 4.5 +/- 0.8 mm for no Pd and the highest one, respectively. The removal efficiency of dyes was examined for methylene blue (MB) and it was shown that after 120 min of irradiation, the removal efficiency reached around 86.4% for the highest contribution of Pd. The pseudo-first-order constant (K-app) increased from 0.0032 to 0.0179 min(-1). The recyclability of Pd-HAP denoted that removal efficiency decreased to 5.65, 8.14, 6.24, 8.76, and 10.2% for different contents of Pd(II) after 6 cycles. (C) 2020 Published by Elsevier B.V. on behalf of King Saud University.