Abstract
The effect of 0.5, 1, 1.5 and 2 wt% Cu addition on the microstructure and mechanical properties of Al-30 wt% Zn alloy has been investigated by stress-strain tests carried out in the temperature range from 508 to 608 K. The work-hardening parameters of the test alloys decreased with increasing the deformation temperature and exhibited discontinuity at 548 K, resulting two deformation temperature regions, the low-temperature region (below 548 K) and high-temperature region (above 548 K). The activation energy of fracture mechanisms has been calculated and found to be 19.6 and 33.2 kJ/mol at the low and high temperature regions respectively. The operating mechanisms of work-hardening of the test alloys were confirmed by the analysis of X-ray diffraction patterns. (C) 2014 Elsevier B.V. All rights reserved.