Abstract
In this study, billets of the ZK30 (Mg-3Zn-0.6 Zr-0.4 Mn, wt%) alloy were Equal Channel Angle Pressing (ECAP) processed for up to four passes of routes Bc (with rotating the sample 90 degrees in the same direction between the subsequent passes), A (without sample rotation), and C (with sample rotating 180 degrees) after each pass at a temperature of 250 degrees C and a ram speed of 10 mm/min using a die with an internal channel angle of 90 degrees. The microstructural evolution and the crystallographic texture were investigated using a Scanning Electron Microscope (SEM) equipped with the Electron Back-Scatter Diffraction (EBSD) technique. Corrosion measurements were conducted in ringer lactate which is a simulated body fluid. The Vickers microhardness test and tensile tests were conducted for the alloy before and after processing. The as-annealed billets exhibited a bimodal structure as fine grains (more than 3.39 mu m) coexisted with almost-equiaxed coarse grains (less than 76.73 mu m); the average grain size was 26.69 mu m. Further processing until four passes resulted in enhanced grain refinement and full Dynamic Recrystallization (DRX). ECAP processing through 4-Bc, 4-A, and 4-C exhibited significant reductions in grain size until they reached 1.94 mu m, 2.89 mu m, and 2.25 mu m, respectively. Four-pass processing also resulted in the transformation of low-angle grain boundaries into high-angle grain boundaries. The previous conclusion was drawn from observing the simultaneous decrease in the fraction of low-angle grain boundaries and an increase in the fraction of high-angle grain boundaries. The pole figures revealed that 4-Bc, 4-A, and 4-C reduced the maximum texture intensity of the as-annealed billets. The potentiodynamic polarization findings revealed that route Bc is the most effective route in improving the corrosion rate, whereas the Electrochemical Impedance Spectroscopy (EIS) revealed that routes A and Bc improved the corrosion resistance with nearly identical values. Finally, 4-Bc resulted in the highest increase in Vickers hardness, yield stress, and ultimate tensile strength with values of 80.8%, 19.3%, and 44.5%, alongside a 31% improvement in ductility, all compared to the AA condition.