Abstract
[Display omitted]
► Treatment of fibre carbon with UV/O3 results in functionalisation of its surface. ► Increasing the surface oxygen content increases the surface coverage of alcohols. ► UV/O3 treatment resulted in three orders of magnitudes increase of surface coverage.
The adsorption properties of untreated, electrochemically treated and ultra-violet/ozone treated polyacrylonitrile based carbon fibres were investigated using temperature programmed desorption (TPD) on a series of linear alcohols as probes in order to understand its surface properties. Surface uptake was found to be sensitive to both the surface treatment and the nature of the adsorbates. Surface coverage increased with increasing alcohol chain due to the increase in their polarizability. It also increased with the level of surface oxygen of the fibres most likely because it facilitates the OH bond dissociation of the alcohol functional group. In addition, the desorption temperature (during TPD) tracked the surface oxygen levels (as determined from XPS O1s signal) suggesting increasing in the adsorption energy. The reactions of C1–C4 linear alcohols were also investigated on the surface of the fibre carbon. The main reaction was dehydrogenation to the corresponding aldehydes; the dehydration reaction to olefins was not observed. The dehydrogenation reaction was sensitive to the length of the alky chain. It was highest for methanol (to formaldehyde) and decreased with increasing the carbon number. Overall TPD of linear alcohols was shown to be a promising method for quantifying the level and strength of bonding occurring on carbon fibre surfaces.