Abstract
•Study the effect of the different pH value on the characteristic's properties of ZnO NSs.•The ZnO nanostructures are grown by M-CBD method using injection air bubbles into growth solution.•Obtain important change in morphology of ZnO from NRs to nano-amber flush rose like ZnO structures.•Found that the crystal size changed from 36.3 nm to 84.33 nm with a various value of pH from 6.7 to 12.•Suitable uses of these different nanostructures for fabricated nanodevices in the future.
In this study, high quality zinc oxide (ZnO) nanostructures were synthesized on glass slide substrates using modified chemical bath deposition (M-CBD) method at low temperature. Through the M-CBD technique the air bubbles will be injected into aqueous growth solution. The RF magnetron sputtering method was utlized to grow ZnO seed layer on the glass substrates. The effect of different pH values of aqueous growth solution on the morphology, elemental chemical composition, crystal structural and the optical properties of ZnO nanostructures have been investigated using field emission-scanning electron microscopy (FE-SEM), Energy dispersive analysis (EDX), X-ray diffraction (XRD), and UV-Visible Spectrometer, respectively. It was observed that altering pH values from acidic to alkaline (basic) by using ammonia solution (NH3) induced the significant change in morphology from nanorods like ZnO to nano-amber flush rose like ZnO structures. Furthermore, increased pH values had an effect on the influence intensity of the preferred orientation plane (002) and average transmittance spectrum. Whilst the absorption band edge has been shifted to a lower energy region due to the quantum size effect. It was also found that the crystal size fluctuated between 36.30 nm and 84.33 nm with a different values of pH from 6.7 to 12. The ZnO synthesized at 6.7 of pH provided the best results regarding the high aspect ratio,structural and optical properties. At this pH value, ZnO growth revealed the nanorod structure with small diameters, size and a higher energy band gap value.