Abstract
Friction stir processing (FSP) has emerged as an effective secondary processing technique to improve the microstructure and properties of aluminum matrix composites (AMCs). Al/(0–15 wt%) Al3Fe AMCs were prepared by adding pure iron powder to molten aluminum and subjected to FSP. The microstructural changes before and after FSP were studied using OM, SEM, EBSD and TEM. Cast composites exhibited coarse grains, segregation, pores and sharp-edged particles. The distribution of particles was rearranged into a homogeneous distribution after FSP. Casting defects such as pores were eliminated. The sharp edges of Al3Fe particles were removed and rounded into near spherical shape. The grain size reduced remarkably due to severe plastic deformation and the pinning effect of reinforced particles. The density of dislocations increased considerably after FSP. The microstructural changes resulted in an improvement of tensile strength and ductility. The possible strengthening mechanisms were reported.
•Friction stir processing of Al/(0–15 wt%) Al3Fe composites.•Total rearrangement of particles into a homogenous distribution occurred.•Polygonal shape Al3Fe particles were broken down into fine sized particles.•Grain size of cast composites were reduced to extremely fine size.•Tensile strength was improved considerably after processing.