Abstract
Nickel-doped poly vinyl alcohol (PVA) films were developed for potential application in industrial sectors like radiation processing. We report in this paper the results of an experimental investigation of Co-60 source yradiation effect on colorimetric, structural and morphological properties of PVA films doped with 0.5% Ni2+ ions (PVA/Ni2+). The PVA/Ni2+ films were irradiated by different gamma-radiation doses varying from 5 to 100 kGy. Color modification of films were studied using L*, a* and b* color space measurements as function of the y-dose and post-irradiation time. The visual change in all samples was verified by microstructure analysis, Fourier transforms infrared (FTIR) spectroscopy, X-Rays diffraction (XRD) and scanning electron microscopy (SEM). The color space exhibited a linear dose response at a dose ranging from 5 to 50 kGy, and then it reached saturation for higher gamma-doses. The calculated color changes (AE) show a linear dose response relationship from 9.90 to 115.02 in the dose range from 0 to 50 kGy. It showed also the activation of stable color centers. The variability of the color change did not exceed 3% during 80 h (h) post-irradiation. Furthermore, the microstructure analysis evidenced that the color modification due to the optical activation of nickel-oxide (NiO) color center were obtained by complexing Ni2+ ions in irradiated PVA films. The obtained results inspire the possibility to use PVA films for the control process in industrial radiation facilities in dose range 5-50 kGy.