Abstract
•Phytic acid effect on collagen solubilization was studied and compared to phosphoric acid.•Overall hydroxyproline release induced by phytic acid was lower compared to phosphoric acid.•Phytic acid has the ability to bind to mineralized and demineralized dentin.•Phytic acid debound from mineralized dentin mostly by the action of urea.•Phytic acid debound from demineralized dentin mostly by the action of ethanol.
To study phytic acid (IP6) effect on collagen solubilization by assessing hydroxyproline (HYP) release, evaluate its binding to demineralized (DD) and mineralized dentin (MD) and determine the effect of different media on debinding of IP6.
Demineralized dentin beams were incubated in 1%, 2% or 3% IP6 and HYP release was evaluated at 1 or 3 weeks and compared to those obtained in untreated control or phosphoric acid (PA)-treated beams. DD or MD powder was treated with 1%, 2% or 3% IP6 and the decrease in IP6 amount was quantitated by ultraviolet–visible spectroscopy. IP6-treated samples were re-suspended in distilled water, ethanol, urea or sodium chloride and the amount of IP6 displaced was determined.
At 1 week, the control group and IP6 showed lower HYP release when compared to PA (P < 0.05). There was no difference among PA, IP6 and control at 3 weeks (P = 0.22). IP6 binding was concentration dependent. 1% IP6 had higher binding potential with MD compared to DD while 2% IP6 showed the opposite result (P<0.05). 3% IP6 had similar binding values between DD and MD (P = 0.53). The highest debinding in MD occurred with urea for 2%, 3% and 1% IP6 in descending manner. Within each concentration of IP6 in DD, the highest debinding effect was reported with ethanol.
IP6 bound to DD and MD in a concentration-dependent manner. IP6 was debound from DD mostly by the action of ethanol, while in MD, urea caused the most displacement. Collagen solubilization of IP6-treated DD was comparable to untreated DD.
These findings add to the potential use of IP6 as an alternative to PA for dentin etching which possibly results in long-term stability of resin-dentin adhesion.