Abstract
We report growth of quaternary Cu-2 ZnSnS4 (CZTS) thin films prepared by the electrochemical deposition from salt precursors containing Cu (II), Zn (II) and Sn (IV) metals. The influence of different sulfurization times t (t=75, 90, 105, and 120 min) on the structural, compositional, morphological, and optical properties, as well as on the electrical properties is studied. The films sulfurized 2 hours showed a prominent kesterite phase with a nearly stoichiometric composition. Samples were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), and Raman and UV-VIS-NIR spectrometer at different stages of work. X-ray diffraction and Raman spectroscopy analyses confirmed the formation of phase-pure CZTS films. (FESEM) shows that compact and dense morphology and enhanced photo-sensitivity. STEM - EDS elemental map of CZTS cross-section confirms homogeneous distribution. From optical study, energy gap was enlarged with a changed sulfurization times in the range of 1.37-1.47 eV.