Abstract
In the present study, zinc oxide (ZnO) nanoparticles were prepared using ZnCl2.2H(2)O as a precursor, via green route using leaf extract of Rhazya stricta as capping and reducing agent. The prepared ZnO nanoparticles were examined using UV-visible spectrophotometer (UV-Vis), Fourier transform infrared spectrometer (FT-IR), X-ray diffraction spectrometer (XRD), and scanning electron microscope (SEM). The UV-Vis absorption spectrum at 355 nm showed an absorption peak, which indicates the formation of ZnO NPs. The FT-IR spectra analysis was performed to identify the potential biomolecule of the as-prepared ZnO NPs. The FT-IR spectra showed peaks at 3455, 1438, 883, and 671 cm(-1) in the region of 4000-500 cm(-1), which indicates -OH, NH, C-H, and M-O groups, respectively. The SEM images showed aggregation of ZnO nanoparticles with an average size of 70-90 nm. The XRD study indicated that the ZnO NPs were crystalline in nature with hexagonal wurtzite structure and broad peaks were observed at 2 theta positions 31.8 degrees, 34.44 degrees, 36.29 degrees, 47.57 degrees, 56.61 degrees, 67.96 degrees, and 69.07 degrees. The synthesized ZnO NPs were found to be good antiplasmodial with a 50% inhibitory concentration (IC50) value of 3.41 mu g/mL. It is concluded from the current study that the ZnO NPs exhibited noble antiplasmodial activity, and for the improvement of antiplasmodial medications, it might be used after further in vivo studies.