Abstract
In this study, the biaxial flexural strength (BFS) and fractography of high/ultra-translucent monolithic zirconia ceramics subjected to different mechanical surface pretreatments were evaluated. A total of 108 disc-shaped samples (12 mm diameter, 1.2 mm thickness) of three zirconia materials (5Y-ZP KATANA Zirconia UTML (ML), 3Y-TZP DD Bio ZX2 (DB), and 5Y-ZP DD cube X2 (DC)) were used. The BFS was investigated after subjecting the samples to surface treatment using air abrasion particles of two types (aluminum oxide or glass microbeads). The data were analyzed using two-way analysis of variance, followed by Scheffe's post hoc test for multiple comparisons. The mean +/- standard deviation BFS for DB was highest after treatment with 50 mu m Al2O3 (1626.05 +/- 31.9 MPa), with lower values being observed following treatment with 50 mu m glass microbeads (1399.53 +/- 24.2 MPa) and in the control sample (1198.51 +/- 21.1 MPa). The mean +/- standard deviation (SD) BFSs for DC and ML were the highest in the control groups. Surface air abrasion with 50 mu m Al2O3 particles and 2 bar pressure is recommended for 3Y-TZP translucent zirconia, while no abrasion of 5Y-ZP translucent zirconia ceramic.