Abstract
Background and Objectives: Khat chewing is considered as a daily habit that is practiced by more than five million people globally. The effect of khat chewing on the surface roughness and the color stability of natural teeth and the material used in the fabrication of dental prosthesis remains unknown. This study was conducted to explore and compare the effect of khat homogenate (KH) on the surface roughness (Ra) and the average color changes (Delta E*) amongst natural teeth and selected shades from different porcelain types, namely, feldspathic metal ceramic (MC) VM13, computer-aided design/computer assisted manufacture (CAD/CAM) feldspathic (Vitablocs Mark II), and multilayer zirconia (Ceramill Zolid PS) porcelains. Materials and Methods: Seventy samples were prepared from natural teeth, feldspathic MC, CAD/CAM Vitablocs Mark II, and zirconia porcelain. The Ra values were measured using a profilometer and expressed in micrometers, whereas the Delta E* values were measured using VITA Easyshade (R) V spectrophotometer for all samples before and after frequent immersion and thermocycling in KH for 30 days. The surface topography was used to assess the materials surfaces (glazed or polished) after KH immersion by using a white light interferometry machine. Results: Results revealed that the Ra and the Delta E* values of the different types of tested porcelain were influenced by KH. The order of surface roughness values was glazed or polished MC > polished Zircon > polished Vitablocs Mark II > natural teeth. The lowest Delta E* values were recorded for glazed Vitablocs Mark II and MC, and the values could be arranged as polished zircon > natural teeth > glazed zircon > polished MC > polished Vitablocs Mark II. P values were significantly varied (<0.001) among all the tested groups, except the zircon group (>0.05) for both Ra and Delta E*. Conclusions: KH significantly affected both surface parameter and color of glazed or polished porcelain materials and natural teeth.