Abstract
The effect of morphology with magnesium (Mg) powder on phase formation and critical current density (J(c),) of sintered (MgB2)-B-11 bulk was studied. As a precursor for the formation of (MgB2)-B-11, the morphology of spherical and plate-like of Mg powder were separately synthesized using atomization and chemical reduction methods. From differential thermal analyses of the sintering process, the solid-solid reaction of a (MgB2)-B-11 sample using spherical Mg powder was confirmed to be much weaker than the plate-like one, and the second exothermic peak place was shifted back and its intensity was increased due to a special microstructure of spherical Mg powder. XRD analysis of (MgB2)-B-11 samples showed that the volume fraction of Mg(11)B(2)in the sintered sample with plate-like Mg was higher than that with the spherical one, and for all the samples (MgB2)-B-11 is the main phase. The Mg(11)B(2 )sample using spherical Mg powder had two different kinds of microstructures because of differences in their diffusivity and their contact interfaces. The J(c) value of an (MgB2)-B-11 sample using spherical Mg powder enhanced the entire field; it was twice as high as that using plate-like Mg, and it was even better than all the J(c) values reported in previous literature using the same kind of Mg powder as precursor.