Abstract
•The highest shear bond strength value was observed in group 1 (non-infected dentin).•The lowest bond strength value was displayed in group 3 (Photodynamic therapy on infected dentin).•Carious dentin showed lower bond strength to composite resin as compared to non-carious dentin.
To evaluate the adhesive bond integrity (shear bond strength-SBS) of composite resin bonded to carious dentin using chlorhexidine gluconate (CHX), Er,Cr:YSGG laser (ECYL) and photodynamic therapy (PDT).
Thirty carious and ten non-carious mandibular teeth were collected through non-traumatic extraction. All samples were embedded in polyvinyl cross-sections to the cemento-enamel junction. The preparation of caries-affected dentin was performed by grinding the specimens using silicon carbide discs. All specimens were randomly allocated in to four groups (n = 10). Group 1, non-affected dentin with no disinfection; Group 2, caries affected dentin treated with 2% CHX; Group 3, affected dentin disinfected with PDT [100 mg/L methylene blue solution (MBS) and Diode laser]; Group 4, affected dentin treated with ECYL. Self-etch adhesive was smeared on all specimens for 10 s and photopolymerized for 10 s. All specimens were placed in an incubator with humid environment for 24 h at 37 °C followed by positioning in universal testing machine for SBS testing. Failure mode examination of debonded samples was performed by a stereomicroscope. Analysis of variance (ANOVA) was used for inter group comparison through mean and standard deviation of each group. For multiple group comparison Tukey HSD was employed. Level of significance was established at p < 0.05.
The highest SBS value was observed in group 1 (24.98 ± 1.59 MPa). Whereas, the lowest bond strength was displayed by group 3 (14.22 ± 1.40 MPa) specimens. Lased dentin in group 4 (15.89 ± 3.22 MPa) exhibited SBS values comparable to group 3 (14.22 ± 1.40 MPa). Group 2 (CHX-18.25 ± 1.29 MPa) exhibited statistically significant difference compared to all experimental groups (p < 0.05).
Adhesive bond strength of disinfected carious dentin was higher with CHX treatment as compared to Photodynamic therapy and Er,Cr: YSGG laser treatment. Carious dentin showed lower bond strength to composite resin as compared to non-carious dentin.