Abstract
•HM presents a critical challenge in terms of management for pediatric dentists.•Carious HM showed lower bond strength compared to non-carious HM.•Bond strength of HM was highest with CHX compared to lasers.
The aim of this study was to investigate the adhesive bond strength and fracture analysis of resin based restorations to carious dentin of hypomineralized molars (HMs) after disinfecting with photodynamic therapy (PDT), Nd:YAG and chlorhexidine (CHX).
Sixty carious HM molars were investigated. After removal of all carious infected tissue, the cavities were condition with methylene blue initiated PDT, a 1064 nm wavelength Nd:YAG laser or 2.0% CHX gel. Non-carious dentin from HM was used as a control without performing any disinfection or conditioning technique. All samples were bonded using a one-step one-coat adhesive bond over the dentin surface, packed with composite and light cured. All specimens were subjected to thermocycling at 5°C and 60°C with a dwell time of 30 s for 10,000 cycles. Bonded specimens were placed on a universal testing machine with a flat loading head. The debonded surface were viewed under light optical microscope to estimate the type of failure including adhesive, cohesive, and admixed.
The highest mean SBS was seen in the non-carious HM (control group). The mean score for control group was 17.64 ± 2.96 MPa. The lowest bond strength value was displayed for Group-PDT (11.37 ± 3.66 MPa) and Group-Nd:YAG (12.69 ± 2.45 MPa). Affected dentin disinfected with the Group-CHX (15.71 ± 3.04 MPa) bonded with composite showed statistically significantly higher SBS values compared to the laser groups (p < 0.05). No statistically significant difference was noted with specimens disinfected with PDT and Nd:YAG laser showed comparable SBS scores (p > 0.05). Fracture analysis showed equal incidence of adhesive and cohesive failures in control group and Group-CHX. Moreover, a significant number of failures in group-PDT were related to adhesive. Whereas in group 4, admixed type failures were common.
Caries infected hypomineralized teeth demonstrated lower bond strength values compared to non-carious hypomineralized teeth. Adhesive bond strength of hypomineralized teeth was highest with chlorhexidine compared to other laser treatment strategies.