Abstract
•The disinfectant capacity of the hematoporphyrin derivative was similar to chlorhexidine.•Co/Cr alloy disinfected with sodium perborate enzyme and citric acid exhibited comparable outcomes against tested microbes.•Metal roughness of Co/Cr used as an alloy did not exhibit significant difference when exposed to chemical disinfectants and photosensitizer.
The present study aimed to evaluate the effect of different cleansers and photodynamic therapy (PDT) on disinfection of Co/Cr removable partial denture colonized with C. albicans, S.aureus and S.mutans.
Twenty-five Co/Cr removable partial dentures were constructed. and inoculated by American Type Culture Collection (ATCC) of Candida albicans, S.aureus, and S.mutans in an in-vitro setup. Co/Cr removable partial dentures were randomly allocated into five groups and framework was immersed in 15 mL of contaminated culture medium broth. Based on the cleansing method, disinfected dentures in group 1 were cleansed with porphyrin derivative; group 2 was exposed to 0.12% chlorhexidine digluconate; samples in group 3 and group 4 were subjected to sodium perborate enzyme and citric acid respectively. Through a surface analyzer, the surface roughness of Co/Cr and methacrylate resin was measured in 3 different zones in micrometers before and after disinfection. Two-way ANOVA and Tukey's test was used to analyze the data. Levene test was used to assess the normal distribution of data. Significance level p< 0.05
The results of metal roughness displayed that Co/Cr used as an alloy did not exhibit significant difference when exposed to different chemical disinfectants and photosensitizer (p > 0.05). Similarly, surface roughness (Ra) of heat polymerized acrylic resin using cleansers and PDT demonstrated no significant difference. Intergroup comparison showed that, hematoporphyrin derivative displayed comparable cleansing property against S. aureus, C.albicans, and S. mutans compared to to 0.12% CHX digluconate (p>0.05). The intragroup comparison showed hematoporphyrin derivative and CHX were equally effective against all bacteria (p>0.05).
CHX digluconate and hematoporphyrin derivative demonstrated high antimicrobial activity against S.aureus, S.mutans, and C.albicans with minimum Ra of an acrylic denture and Co/Cr metallic framework.