Abstract
Series of polymer nanocomposites films consisting of pretreated multiwalled carbon nanotubes (PT-MWCNTs) and poly (vinyl alcohol) (PVA) were prepared at room temperature. The MWCNTs were initially pretreated with 1.0 M sulfuric acid (PT-MWCNTs) and then allowed to disperse in aqueous solutions at different pH values (2-14). It was found that the dispersion of the PT-MWCNTs is a pH dependent. The best PT-MWCNTs dispersion was obtained at pH = 10. Films of PT-MWCNTs/PVA, at this optimum pH-value, were then prepared by casting technique at different PT-MWCNTs weight fractions. The resulted PT-MWCNTs/PVA films were characterized through the direct visualization, Fourier transform infrared, and morphology test. Besides, current-voltage and direct current electrical conductivity for PT-MWCNTs/PVA nanocomposites at 60 degrees C showed that the conductivity mechanism was ohmic and the percolation threshold was around 0.8 wt% PT-MWCNTs. Optical results showed that PT-MWCNTs are homogeneously distributed in the neat PVA and optical gap is significantly decreased from 4.40 to 2.96 eV.