Abstract
Nano-crystalline Zn, Ni and Zn-Ni alloys were prepared as electro-deposited layers on copper substrates. The obtained materials were characterized morphologically and chemically by XRD and scanning electron microscopy, SEM, coupled with EDAX analysis. The electrochemical properties were investigated in KOH solutions by polarization measurements, cyclic voltammetry and EIS techniques. Special emphases were subjected to the hydrogen evolution reaction, HER, on the electrodeposited materials. It was found that the electro-deposited Zn-Ni alloy cathodes possess high catalytic activity for hydrogen evolution in alkaline solutions, which was found to depend on the microstructure and surface morphology of the deposited layer. The high electro-catalytic activity was attributed to the increased surface area of the deposited layers and the number of active sites therein. The increase of the Ni content up to ≈50 at% in the deposited cathode leads to a decrease in the hydrogen evolution overpotential. The highest rate of hydrogen evolution was recorded on Zn-Ni deposits with ≈50 at% Ni. The electrochemical polarization measurements were confirmed by impedance experiments, and the experimental impedance data were fitted to theoretical data according to a proposed model for the electrode/electrolyte interface.
[Display omitted]
•Zn-51%Ni catalysts show high electro-catalytic activity for the HER.•They are used in 1.0 M KOH solution without any special treatment.•The electrode has the lowest resistance for the HER.•It is very stable for more than 4 weeks and no corrosion was recorded.•The rate of hydrogen production is constant over weeks of application.